  Our University: a
  • Our University home
  • Vice Chancellor's welcome
  • New University Chancellor
  • About us
  • Our governance
  • Our colleges and schools
  • Professional Services
  • Facts and statistics
  • Our services
•  
  community where
  • Community home
  • University campus
  • On campus events
  • Campus development
  • Regional relationships
  • University School
•  
  students,
  • Study at Birmingham
  • Course finder
  • Entry requirements
  • English for International Students Unit
  • Request a prospectus
  • Fees and funding
  • Accommodation
  • Careers
  • Teaching and learning
  • Student support
  • Why Birmingham?
  • Visit us
  • Teachers, Careers Advisors and Parents
  • Studying abroad
•  
  partners,
  • Partners home
  • Services to business
  • Recruiting our students to work for you
  • International partners and collaborations
  • Conferences
•  
  alumni,
  • Alumni home
  • Staying in touch
  • Giving
  • Get involved
  • Alumni benefits
  • Alumni news
  • Events and reunions
  • Our Alumni
  • Family community
•  
  staff and our
  • Staff home
  • About Birmingham
  • Why work here?
  • Jobs
  • Encouraging excellence
  • Staff search
•  
  research create
  • Research home
  • Our research
  • Our impact
  • Supporting research
  • Partners and collaborators
  • The Institute of Advanced Studies
  • Funding and awards
  • Birmingham Heroes
  • Research activitiy
  • Jobs
•  
  international impact
  • International home
  • Our global impact
  • International students
  • International collaborations
  • International visitors
  • Meet us
  • Study abroad

Theoretical Predictions

Theoretical Simulation Gallery.

This page shows some results of oxidation-driven solute depletion simulations obtained using the Group's ODIN software (see publications page for reference).

 

Al depletion at the edge of a FeCrAlY sample after 0.1 hours at 1200ºC.

 

Al depletion at the re-entrant edge of a FeCrAlY sample after 0.1 hours at 1200ºC.

Al concentration in the corner of a 50-micron MCrAlY overlay coating after 5 hours at 1100ºC.

Al depletion around cooling holes through NiCrAl after 1000 hours at 1200ºC (hole separation is approximately 420 microns).

Al concentration in and around a 2D protuberance on a 100-micron MCrAlY coating after 1 hour of oxidation at 1100ºC.